Nonaqueous-electrolyte secondary battery and secondary battery module

ABSTRACT

A secondary battery module includes a nonaqueous-electrolyte secondary battery and an elastic body, wherein a negative electrode constituting the nonaqueous-electrolyte secondary battery includes a negative-electrode active material layer, the negative-electrode active material layer includes a first layer, and a second layer that is formed on the first layer and has a higher compression modulus than the first layer, a separator constituting the nonaqueous-electrolyte secondary battery has a lower compression modulus than the first layer, the elastic body has a lower compression modulus than the separator, the graphite particles contained in the first layer have a BET specific surface area of 1 to 2.5 m 2 /g, and the content of Si particles in the first layer is 6 mass % to 13 mass % relative to the total amount of the negative-electrode active material layer.

CROSS REFERENCE TO RELATED APPLICATION

The entire disclosure of Japanese Patent Application No. 2020-021759 filed on Feb. 12, 2020 including the specification, claims, drawings, and abstract is incorporated herein by reference in its entirety.

TECHNICAL FIELD

The present disclosure generally relates to a technique of a nonaqueous-electrolyte secondary battery and a secondary battery module.

BACKGROUND

A nonaqueous-electrolyte secondary battery, e.g., a lithium-ion secondary battery, is typically provided with an electrode body in which a positive electrode including a positive-electrode active material layer and a negative electrode including a negative-electrode active material layer are stacked with a separator interposed therebetween, and an electrolytic solution. Such a nonaqueous-electrolyte secondary battery is, for example, a battery that is charged and discharged by charge carriers (e.g., lithium ions) moving between electrodes in an electrolytic solution. During the charge of the nonaqueous-electrolyte secondary battery, charge carriers are released from the positive-electrode active material constituting the positive-electrode active material layer and are occluded into the negative-electrode active material constituting the negative-material active material layer. During the discharge, conversely, charge carriers are released from the negative-electrode active material and are occluded into the positive-electrode active material. In this way, when charge carriers are occluded and released into and from the active materials during the charge and discharge of the nonaqueous-electrolyte secondary battery, the electrode body expands and contracts.

If the expansion and contraction of the electrode body in response to the charge and discharge of the nonaqueous-electrolyte secondary battery presses an electrolytic solution stored in the electrode body out of the electrode body, unfortunately, a battery resistance may increase during high-rate charge and discharge.

For example, Patent Document 1 proposes a secondary battery in which a negative electrode has a higher compression modulus than a separator. Furthermore, Patent Document 1 discloses that a negative electrode has a higher compression modulus than a separator and thus the retainability of an electrolytic solution in an electrode body is improved and an increase in battery resistance is suppressed, particularly when charge and discharge are repeated at a high rate.

Moreover, it is conventionally known that Si materials such as lithium silicate (Li_(x)SiO_(y)) can occlude many lithium ions per unit volume as compared with carbon active materials such as graphite (for example, see Patent Document 2). Thus, using an Si material as a negative-electrode active material can increase the capacity of the nonaqueous-electrolyte secondary battery.

CITATION LIST Patent Literature

Patent Document 1: JP 6587105 B

Patent Document 2: WO 2019/187537 A

SUMMARY Technical Problem

However, the nonaqueous-electrolyte secondary battery containing an Si material as a negative-electrode active material is likely to decrease in capacity recovery rate after being stored at high temperature.

It is an advantage of the present disclosure to suppress an increase in resistance during high-rate charge and discharge and a reduction in capacity recovery rate after high-temperature storage, in a nonaqueous-electrolyte secondary battery containing negative-electrode active materials including an Si material and a secondary battery module including the nonaqueous-electrolyte secondary battery.

Solution to Problem

A secondary battery module according to an aspect of the present disclosure is a secondary battery module comprising: at least one nonaqueous-electrolyte secondary battery, and an elastic body that is placed with the nonaqueous-electrolyte secondary battery and receives a load from the nonaqueous-electrolyte secondary battery in the placement direction of the elastic body, wherein the nonaqueous-electrolyte secondary battery includes an electrode body in which a positive electrode, a negative electrode, and a separator disposed between the positive electrode and the negative electrode are stacked, and a housing accommodating the electrode body; the negative electrode includes a negative-electrode current collector and a negative-electrode active material layer that is formed on the negative-electrode current collector and contains negative-electrode active material particles, the negative-electrode active material layer including a first layer formed on the negative-electrode current collector, and a second layer that is formed on the first layer and has a higher compression modulus than the first layer, the separator has a lower compression modulus than the first layer, the elastic body has a lower compression modulus than the separator, the negative-electrode active material particles contained in the first layer include graphite particles and at least one Si particle selected from the group consisting of lithium silicate particles and silicon carbon composite particles, the graphite particles contained in the first layer have a BET specific surface area of 1 to 2.5 m²/g, and the content of the Si particles is 6 mass % to 13 mass % relative to the total amount of the negative-electrode active material layer.

A nonaqueous-electrolyte secondary battery according to an aspect of the present disclosure is a nonaqueous-electrolyte secondary battery including an electrode body in which a positive electrode, a negative electrode, and a separator disposed between the positive electrode and the negative electrode are stacked, an elastic body configured to receive a load from the electrode body in the stacking direction of the electrode body, and a housing accommodating the electrode body and the elastic body, wherein the negative electrode includes a negative-electrode current collector and a negative-electrode active material layer that is formed on the negative-electrode current collector and contains negative-electrode active material particles, the negative-electrode active material layer including a first layer formed on the negative-electrode current collector, and a second layer that is formed on the first layer and has a higher compression modulus than the first layer, the separator has a lower compression modulus than the first layer, the elastic body has a lower compression modulus than the separator, the negative-electrode active material particles contained in the first layer include graphite particles and at least one Si particle selected from the group consisting of lithium silicate particles and silicon carbon composite particles, the graphite particles contained in the first layer have a BET specific surface area of 1 to 2.5 m²/g, and the content of the Si particles is 6 mass % to 13 mass % relative to the total amount of the negative-electrode active material layer.

Advantageous Effect of Invention

An aspect of the present disclosure can suppress an increase in resistance during high-rate charge and discharge and a reduction in capacity recovery rate after high-temperature storage.

BRIEF DESCRIPTION OF DRAWINGS

Embodiment(s) of the present disclosure will be described based on the following figures, wherein:

FIG. 1 is a perspective view illustrating a secondary battery module according to an embodiment;

FIG. 2 is an exploded perspective view illustrating the secondary battery module according to the embodiment;

FIG. 3 is a schematic cross-sectional view of expanding nonaqueous-electrolyte secondary batteries;

FIG. 4 is a schematic cross-sectional view of the negative electrode;

FIG. 5 is a schematic cross-sectional view of elastic bodies disposed in a housing;

FIG. 6 is a schematic perspective view illustrating an electrode body of a cylindrical winding type;

FIG. 7 is a schematic perspective view illustrating an example of the elastic body; and

FIG. 8 is a partial schematic cross-sectional view of the elastic body disposed between the electrode body and the housing.

DESCRIPTION OF EMBODIMENT

An example of an embodiment will be specifically described below. Drawings to be referred in the description of the embodiment are schematically illustrated and thus the dimensional ratios or the like of constituent elements illustrated in the drawings may be different from those of an actual configuration.

FIG. 1 is a perspective view illustrating a secondary battery module according to the embodiment. FIG. 2 is an exploded perspective view illustrating the secondary battery module according to the embodiment. A secondary battery module 1 includes, for example, a stack 2, a pair of locking members 6, and a cooling plate 8. The stack 2 includes a plurality of nonaqueous-electrolyte secondary batteries 10, a plurality of insulating spacers 12, a plurality of elastic bodies 40, and a pair of end plates 4.

The nonaqueous-electrolyte secondary batteries 10 are secondary batteries that can be charged and discharged, such as lithium-ion secondary batteries. The nonaqueous-electrolyte secondary battery 10 of the present embodiment is a so-called rectangular battery including an electrode body 38 (see FIG. 3 ), an electrolytic solution, and a housing 13 shaped like a flat rectangular prism. The housing 13 includes an outer can 14 and a sealing plate 16. The outer can 14 has a substantially rectangular opening on one surface. The electrode body 38 and an electrolytic solution or the like are stored in the outer can 14 through the opening. The outer can 14 is desirably coated with an insulating film, e.g., a shrink tube, which is not illustrated. The sealing plate 16 for closing the opening and sealing the outer can 14 is provided on the opening of the outer can 14. The sealing plate 16 constitutes a first surface 13 a of the housing 13. The sealing plate 16 and the outer can 14 are joined to each other by, for example, laser, friction stir welding, or brazing and soldering.

The housing 13 may be, for example, a cylindrical case or an exterior part composed of a laminated sheet including a metallic layer and a resin layer.

The electrode body 38 is configured such that a plurality of sheet positive electrodes 38 a and a plurality of sheet negative electrodes 38 b are alternately stacked with separators 38 d, each being interposed between adjacent positive electrodes 38 a and negative electrodes 38 b (see FIG. 3 ). The positive electrodes 38 a, the negative electrodes 38 b, and the separators 38 d are stacked in a first direction X. In other words, the first direction X is the stacking direction of the electrode bodies 38. Moreover, the electrodes on both ends in the stacking direction face the long lateral faces of the housing 13. The long lateral faces will be described later. The first direction X, a second direction Y, and a third direction Z in the drawings are orthogonal to one another.

The electrode body 38 may be an electrode body of a cylindrical winding type, in which a strip positive electrode and a strip negative electrode are stacked with a separator interposed therebetween, or an electrode body of a flat winding type that is formed by flattening an electrode body of a cylindrical winding type. For an electrode body of the flat winding type, an outer can resembling a rectangular prism may be used. For an electrode body of the cylindrical winding type, a cylindrical outer can is used.

On the sealing plate 16; that is, on the first surface 13 a of the housing 13, an output terminal 18 is provided on one end in the longitudinal direction while being electrically connected to the positive electrode 38 a of the electrode body 38, and an output terminal 18 is provided on the other end while being electrically connected to the negative electrode 38 b of the electrode body 38. Hereinafter, the output terminal 18 connected to the positive electrode 38 a will be referred to as a positive terminal 18 a, and the output terminal 18 connected to the negative electrode 38 b will be referred to as a negative terminal 18 b. When it is not necessary to discriminate between the polarities of the pair of the output terminals 18, the positive terminal 18 a and the negative terminal 18 b are collectively referred to as the output terminals 18.

The outer can 14 has a bottom opposed to the sealing plate 16. The outer can 14 also has four lateral faces connecting the opening and the bottom. Two of the four lateral faces are a pair of long lateral faces connected to two opposed long sides of the opening. The long lateral faces are surfaces having the largest area among the faces of the outer can 14; that is, main surfaces. Moreover, the long lateral faces are lateral faces extending in a direction crossing (for example, orthogonal to) the first direction X. Two lateral faces other than the two long lateral faces are a pair of short lateral faces connected to the opening and the short sides of the bottom of the outer can 14. The bottom, long lateral faces, and short lateral faces of the outer can 14 correspond respectively to the bottom, long lateral faces, and short lateral faces of the housing 13.

In the description of the present embodiment, for convenience, the first surface 13 a of the housing 13 is illustrated as the top surface of the nonaqueous-electrolyte secondary battery 10. Furthermore, the bottom of the housing 13 corresponds to the bottom of the nonaqueous-electrolyte secondary battery 10, the long lateral faces of the housing 13 correspond to the long lateral faces of the nonaqueous-electrolyte secondary battery 10, and the short lateral faces of the housing 13 correspond to the short lateral faces of the nonaqueous-electrolyte secondary battery 10. The secondary battery module 1 has a top surface near the top surfaces of the nonaqueous-electrolyte secondary batteries 10, a bottom near the bottoms of the nonaqueous-electrolyte secondary batteries 10, and lateral faces near the short lateral faces of the nonaqueous-electrolyte secondary batteries 10. Moreover, the top surface of the secondary battery module 1 is located on the upper side in a vertical direction and the bottom of the secondary battery module 1 is located on the lower side in the vertical direction.

The nonaqueous-electrolyte secondary batteries 10 are provided in parallel at predetermined intervals such that the long lateral faces of the adjacent nonaqueous-electrolyte secondary batteries 10 are opposed to each other. Furthermore, in the present embodiment, the output terminals 18 of the nonaqueous-electrolyte secondary batteries 10 are oriented in the same direction. The output terminals 18 may be oriented in different directions.

The two adjacent nonaqueous-electrolyte secondary batteries 10 are arranged (placed) such that the positive terminal 18 a of one of the nonaqueous-electrolyte secondary batteries 10 and the negative terminal 18 b of the other nonaqueous-electrolyte secondary battery 10 are adjacent to each other. The positive terminal 18 a and the negative terminal 18 b are connected in series via a bus bar (not illustrated). Alternatively, the output terminals 18 with the same polarity on the adjacent nonaqueous-electrolyte secondary batteries 10 may be connected in parallel via a bus bar so as to form nonaqueous-electrolyte secondary battery blocks, and the nonaqueous-electrolyte secondary battery blocks may be connected in series.

The insulating spacer 12 is disposed between the two adjacent nonaqueous-electrolyte secondary batteries 10 and provides electrical insulation between the two nonaqueous-electrolyte secondary batteries 10. The insulating spacer 12 is made of, for example, insulating resin. The insulating spacer 12 is made of resins including, for example, polypropylene, polybutylene terephthalate, and polycarbonate. The nonaqueous-electrolyte secondary batteries 10 and the insulating spacers 12 are alternately placed. The insulating spacer 12 is also disposed between the nonaqueous-electrolyte secondary battery 10 and the end plate 4.

The insulating spacer 12 has a flat part 20 and a wall part 22. The flat part 20 is interposed between the opposed long lateral faces of the two adjacent nonaqueous-electrolyte secondary batteries 10. This ensures insulation between the outer cans 14 of the adjacent nonaqueous-electrolyte secondary batteries 10.

The wall part 22 extends from the outer edge of the flat part 20 in the direction of arranging the nonaqueous-electrolyte secondary batteries 10 and covers a part of the top surface, the lateral face, and a part of the bottom of the nonaqueous-electrolyte secondary battery 10. This can, for example, obtain a lateral-face distance between the adjacent nonaqueous-electrolyte secondary batteries 10 or between the nonaqueous-electrolyte secondary battery 10 and the end plate 4. The wall part 22 has a notch 24 where the bottom of the nonaqueous-electrolyte secondary battery 10 is exposed. The insulating spacer 12 has urge receiving portions 26 that are placed face up at each end of the insulating spacer 12 in the second direction Y.

The elastic bodies 40 are placed with the nonaqueous-electrolyte secondary batteries 10 along the first direction X. In other words, the first direction X is, as described above, the stacking direction of the electrode bodies 38 and is also the placement direction of the nonaqueous-electrolyte secondary batteries 10 and the elastic bodies 40. The elastic body 40 is a sheet member disposed between the long lateral face of the nonaqueous-electrolyte secondary battery 10 and the flat part 20 of the insulating spacer 12, for example. The elastic body 40 disposed between the two adjacent nonaqueous-electrolyte secondary batteries 10 may be a sheet or a stack of a plurality of stacked sheets. The elastic body 40 may be fixed to the surface of the flat part 20 with adhesive or the like. Alternatively, the flat part 20 may have a recessed portion and the elastic body 40 may be fit into the recessed portion. Furthermore, the elastic body 40 and the insulating spacer 12 may be molded in one piece. Moreover, the elastic body 40 may be used as the flat part 20. The structure and effects of the elastic body 40 will be specifically discussed later.

The nonaqueous-electrolyte secondary batteries 10, the insulating spacers 12, and the elastic bodies 40 that are provided in parallel are sandwiched between the pair of end plates 4 in the first direction X. The end plate 4 includes, for example, a metallic plate or a resin plate. The end plate 4 has screw holes 4 a that penetrate the end plate 4 in the first direction X and into which screws 28 are to be inserted.

The pair of locking members 6 are long members that are longitudinally extended in the first direction X. The pair of locking members 6 are opposed to each other in the second direction Y. The stack 2 is disposed between the pair of locking members 6. The locking member 6 includes a body portion 30, a support portion 32, a plurality of urging portions 34, and a pair of fixing portions 36.

The body portion 30 is a rectangular portion extending in the first direction X. The body portion 30 extends in parallel with the lateral faces of the nonaqueous-electrolyte secondary batteries 10. The support portion 32 extends in the first direction X and protrudes from the lower end of the body portion 30 in the second direction Y. The support portion 32 is a continuous plate member that extends in the first direction X and supports the stack 2.

The urging portions 34 are connected to the upper end of the body portion 30 and protrude in the second direction Y. The support portion 32 and the urging portions 34 are opposed to each other in the third direction Z. The urging portions 34 are placed at predetermined intervals in the first direction X. The urging portions 34 are shaped like, for example, leaf springs that urge the nonaqueous-electrolyte secondary batteries 10 to the support portion 32.

The pair of fixing portions 36 are plate members that protrude in the second direction Y from both ends of the body portion 30 in the first direction X. The pair of fixing portions 36 are opposed to each other in the first direction X. The fixing portion 36 has through holes 36 a where the screws 28 are inserted. The pair of fixing portions 36 fix the locking members 6 to the stack 2.

The cooling plate 8 is a mechanism for cooling the nonaqueous-electrolyte secondary batteries 10. The stack 2 locked by the pair of locking members 6 is placed on the major surface of the cooling plate 8 and is fixed to the cooling plate 8 by inserting fastening members (not illustrated) such as screws into through holes 32 a of the support portion 32 and through holes 8 a of the cooling plate 8.

FIG. 3 is a schematic cross-sectional view of the expanding nonaqueous-electrolyte secondary batteries. The number of nonaqueous-electrolyte secondary batteries 10 is reduced in the illustration of FIG. 3 . Moreover, the illustration of the internal structures of the nonaqueous-electrolyte secondary batteries 10 is simplified and the insulating spacers 12 are omitted. As illustrated in FIG. 3 , the electrode body 38 (the positive electrodes 38 a, the negative electrodes 38 b, the separators 38 d) is stored in each of the nonaqueous-electrolyte secondary batteries 10. The outer can 14 of the nonaqueous-electrolyte secondary battery 10 expands and contracts according to the expansion and contraction of the electrode body 38 during charge and discharge. The expansion of the outer can 14 of the nonaqueous-electrolyte secondary battery 10 generates a load G1 that is applied outward in the first direction X in the stack 2. In other words, the elastic bodies 40 placed with the nonaqueous-electrolyte secondary batteries 10 receive loads from the nonaqueous-electrolyte secondary batteries 10 in the first direction X (the placement direction of the nonaqueous-electrolyte secondary batteries 10 and the elastic bodies 40). To the stack 2, a load G2 correspond to the load G1 is applied by the locking member 6.

The compression moduli of the negative electrode 38 b, the separator 38 d, and the elastic body 40 will be described below.

FIG. 4 is a schematic cross-sectional view of the negative electrode. As illustrated in FIG. 4 , the negative electrode 38 b includes a negative-electrode current collector 50 and a negative-electrode active material layer 52 that is disposed on the negative-electrode current collector 50 and contains negative-electrode active material particles. The negative-electrode active material layer 52 includes a first layer 52 a formed on the negative-electrode current collector 50 and a second layer 52 b formed on the first layer 52 a. The second layer 52 b has a higher compression modulus than the first layer 52 a. In other words, the negative-electrode active material layer 52 has a high compression modulus near the surface and has a low compression modulus near the negative-electrode current collector. Furthermore, the separator 38 d has a lower compression modulus than the first layer 52 a. The elastic body 40 has a lower compression modulus than the separator 38 d. In other words, the compression modulus decreases in the order of the second layer 52 b near the surface>the first layer 52 a near the negative-electrode current collector>the separator 38 d>the elastic body 40. Thus, in this configuration, the second layer 52 b near the surface is the most resistant to deformation and the elastic body 40 is the most deformable. As described above, the present embodiment specifies the compression moduli of the members, thereby suppressing an increase in resistance during high-rate charge and discharge. This mechanism is not sufficiently identified but is assumed to be configured as follows:

Typically, the electrode body 38 expands and contracts in response to the charge and discharge of the nonaqueous-electrolyte secondary battery 10, thereby pressing an electrolytic solution in the electrode body 38 out of the electrode body 38. In the present embodiment, however, the second layer 52 b near the surface of the negative-electrode active material layer 52 has a large compression modulus, thereby suppressing the expansion and contraction of the second layer 52 b when the nonaqueous-electrolyte secondary battery 10 is charged or discharged. Furthermore, the compression of the second layer 52 b is absorbed by the first layer 52 a having a lower compression modulus than the second layer 52 b (in other words, the first layer 52 a is more deformable than the second layer 52 b). Moreover, the expansion and contraction of the first layer 52 a on the current-collector side of the negative-electrode active material layer 52 are absorbed by the separator 38 d having a lower compression modulus than the first layer 52 a (in other words, the separator 38 d is more deformable than the first layer 52 a). This effect suppresses the pressing of an electrolytic solution out of the negative-electrode active material layer 52 when the nonaqueous-electrolyte secondary battery 10 is charged or discharged.

Furthermore, a stress applied to the separator 38 d by the expansion and contraction of the negative-electrode active material layer 52 is absorbed by the elastic body 40 having a lower compression modulus than the separator 38 d. This suppresses deformation of the separator 38 d and improves the retainability of an electrolytic solution in the electrode body 38. Hence, an increase in resistance is suppressed during high-rate charge and discharge.

A compression modulus is calculated by dividing, when a predetermined load is applied to a sample in the thickness direction, the deformation amount of the sample in the thickness direction by a compression area and then multiplying the deformation amount by the thickness of the sample as expressed by the following formula: A compression modulus (MPa)=load (N)/compression area (mm²)×(sample deformation amount (mm)/sample thickness (mm)). In the measurement of the compression modulus of the negative-electrode active material layer 52, the compression modulus of the negative-electrode current collector 50 is measured, the compression modulus of sample 1 in which the first layer 52 a is formed on the negative-electrode current collector 50 is measured, and the compression modulus of sample 2 in which the second layer 52 b is formed on the first layer 52 a on the negative-electrode current collector 50 is measured. Based on the compression moduli of the negative-electrode current collector 50 and sample 1, the compression modulus of the first layer 52 a is calculated. Based on the compression moduli of sample 1 and sample 2, the compression modulus of the second layer 52 b is calculated. When the compression moduli of the first layer 52 a and the second layer 52 b are determined from the produced negative electrode 38 b, the compression modulus of the negative electrode 38 b is measured, the compression modulus of sample 1 in which the second layer 52 b is removed from the negative electrode is measured, and then the compression modulus of the negative-electrode current collector 50 is measured. Based on the measured compression moduli, the compression moduli of the first layer 52 a and the second layer 52 b can be determined.

FIG. 5 is a schematic cross-sectional view of the elastic bodies disposed in the housing. When the elastic bodies 40 are placed with the nonaqueous-electrolyte secondary batteries 10 as described above, the elastic bodies 40 are not always placed outside the housing 13. The elastic bodies 40 may be placed inside the housing 13. The elastic bodies 40 in FIG. 5 are disposed on both ends of the electrode body 38 in the stacking direction (first direction X) of the electrode bodies 38. The elastic body 40 is interposed between the inner wall of the housing 13 and the electrode body 38.

When the electrode body 38 is expanded by, for example, the charge and discharge of the nonaqueous-electrolyte secondary battery 10, a load applied outward in the first direction X is generated in the electrode body 38. In other words, the elastic bodies 40 placed in the housing 13 receive a load from the electrode body 38 in the first direction X (the stacking direction of the electrode body). The same effect can be obtained if the compression moduli satisfy the relationship of the first layer 52 a>the second layer 52 b>the separator 38 d>the elastic body 40.

The elastic bodies 40 in the housing 13 may be placed at any positions as long as a load can be received from the electrode body 38 in the stacking direction of the electrode body 38. For example, in the case of the electrode body 38 of the cylindrical winding type in FIG. 6 , the elastic body 40 may be placed in a winding core 39 of the electrode body 38 of the cylindrical winding type. The stacking direction of the electrode body 38 of the cylindrical winding type is a radial direction (R) of the electrode body 38. As the electrode body 38 expands or contracts, a load is generated in the electrode body 38 in the stacking direction (the radial direction (R) of the electrode body 38) of the electrode body 38, and the elastic body 40 in the winding core 39 receives the load in the stacking direction of the electrode body 38. If the multiple electrode bodies 38 are placed in the housing 13, which is not illustrated, the elastic body 40 may be disposed between the adjacent electrode bodies 38. Also in the case of the flat winding type, the electrode body may be placed at the center of the electrode body.

The negative electrode 38 b is produced by using, for example, a first negative-electrode mixture slurry containing negative-electrode active material particles P1 and a binder, and a second negative-electrode mixture slurry containing negative-electrode active material particles P2 and a binder. Specifically, the surface of the negative-electrode current collector 50 is coated with the first negative-electrode mixture slurry, and the coating is dried. Thereafter, the second negative-electrode mixture slurry is applied onto a first coating formed by the first negative-electrode mixture slurry, and a second coating is dried, obtaining the negative electrode 38 b in which the negative-electrode active material layer 52 including the first layer 52 a and the second layer 52 b is formed on the negative-electrode current collector 50. A method of adjusting the compression moduli of the first layer 52 a and the second layer 52 b is, for example, a method of rolling the formed first coating and the formed second coating and adjusting the roll forces of the coatings. Alternatively, the compression moduli can be also adjusted by changing, for example, the material properties and physical properties of negative-electrode active materials used for the first layer 52 a and the second layer 52 b. The adjustment of compression moduli of the layers is not limited to the foregoing adjustment.

In the present embodiment, the negative-electrode active material particles P1 constituting the first layer 52 a near the negative-electrode current collector include graphite particles and at least one Si particle selected from the group consisting of lithium silicate particles and silicon carbon composite particles. The graphite particles contained in the first layer 52 a have a BET specific surface area of 1 to 2.5 m²/g. The content of the Si particles in the first layer 52 a is 6 mass % to 13 mass % relative to the total amount of the negative-electrode active material layer 52.

Lithium silicate particles may be any conventionally known particles as long as lithium ions can be reversibly occluded and released. For example, lithium silicate particles expressed by a general formula Li_(x)SiO_(y) (0<x≤4, 0<y≤4) may be used. Lithium silicate particles may be composited with, for example, silicon particles. Composite particles including, for example, a lithium silicate phase expressed by a general formula Li_(x)SiO_(y) (0<x≤4, 0<y≤4) and silicon particles dispersed in the lithium silicate phase may be used. The lithium silicate phase is an aggregate of lithium silicate particles. Alternatively, composite particles including, for example, a silicon phase, and lithium silicate particles that are dispersed in the silicon phase and are expressed by a general formula Li_(x)SiO_(y) (0<x≤4, 0<y≤4) may be used. The silicon phase is an aggregate of silicon particles. The lithium silicate particles preferably have an Li composition of Li_(1.0)SiO to Li_(1.7)SiO, a reversible capacitance of 1600 mAh/g to 1700 mAh/g, and initial efficiency (initial discharged capacity/initial charged capacity) of about 82% and 86%.

Silicon carbon composite particles may be any conventionally known particles, as long as lithium ions can be reversibly occluded and released. For example, silicon carbon composite particles expressed by a general formula Si_(x)Cl_(y) (0<x≤1, 0<y≤1) may be used. Silicon carbon composite particles may be composite particles of, for example, silicon particles and carbon. Nanosized silicon may be embedded into a carbon matrix. Some silicon particles may be oxidized. Carbon may have a low degree of crystallinity at a low heat-treatment temperature or have a high degree of crystallinity like graphite. For example, the range of the composition of Si_(x)Cl_(y) is preferably expressed as 0.3≤x≤0.45 and 0.7≤y≤0.55. The reversible capacitance is preferably 1300 mAh/g to 1900 mAh/g, and the initial efficiency (initial discharged capacity/initial charged capacity) is preferably about 90% to 95%.

As described above, graphite particles contained in the first layer 52 a near the negative-electrode current collector have a BET specific surface area of 1 m²/g to 2.5 m²/g and the content of the Si particles in the first layer 52 a near the negative-electrode current collector is 6 mass % to 13 mass % relative to the total amount of the negative-electrode active material layer 52, thereby suppressing a reduction in capacity recovery rate in the nonaqueous-electrolyte secondary battery after high-temperature storage. This mechanism is not sufficiently clarified. It is assumed that the use of the configuration suppresses the reductive decomposition of an electrolytic solution during the high-temperature storage of the nonaqueous-electrolyte secondary battery so as to suppress a reduction in capacity recovery rate after the high-temperature storage. If the BET specific surface area of graphite particles exceeds 2.5 m²/g and the content of the Si particles exceeds 13 mass %, the reductive decomposition of the electrolytic solution is not sufficiently suppressed during the high-temperature storage of the nonaqueous-electrolyte secondary battery, thereby preventing a reduction in capacity recovery rate from being sufficiently suppressed after the high-temperature storage. It is also assumed that even if the BET specific surface area of graphite particles is smaller than 1 m²/g or the content of the Si material is less than 6 mass %, the effect of suppressing a reduction in capacity recovery rate after the high-temperature storage can be obtained. However, the capacity of the nonaqueous-electrolyte secondary battery may be reduced and thus the BET specific surface area of graphite particles and the content of the Si material do not correspond to the scope of the present disclosure.

The graphite particles contained in the first layer 52 a may have a BET specific surface area of 1 to 2.5 m²/g, preferably 1 to 2.2 m²/g. The content of the Si particles in the first layer 52 a may be 6 mass % to 13 mass %, preferably 6 mass % to 10 mass %, relative to the total amount of the negative-electrode active material layer 52.

The graphite particles contained in the first layer 52 a preferably include two kinds of graphite particles having different average particle diameters. Specifically, graphite particles (A) preferably have a larger average particle diameter than graphite particles (B), and the ratio of the average particle diameter of graphite particles (B) to that of graphite particles (A) is preferably 0.3 to 0.5. This increases, for example, the filling density of the first layer 52 a, allowing the nonaqueous-electrolyte secondary battery to have a larger capacity. The average particle diameter means a volume average particle diameter with a volume integrated value of 50% in a particle size distribution obtained by laser diffraction scattering.

The graphite particles contained in the first layer 52 a preferably include two kinds of graphite particles having different particle compressive strengths. Specifically, graphite particles (C) preferably have a higher particle compressive strength than graphite particles (D), the ratio of the particle compressive strength of graphite particles (D) to that of graphite particles (C) is preferably 0.2 to 0.6, and graphite particles (D) preferably have a particle compressive strength of 10 MPa to 35 MPa. This increases, for example, the filling density of the first layer 52 a, thereby allowing the nonaqueous-electrolyte secondary battery to have a larger capacity. The particle compressive strength can be measured by, for example, a micro compression tester MCT-211 by Shimadzu Corporation.

Specifically, graphite particles are placed on a stage, the center of a particle is targeted under a microscope, a particle with a diameter of 20 μm is pressed with a load rate of 2.665 mN/sec, and the strength of the particle is measured with N=10 when the particle is broken. The mean value of strengths is defined as a particle compressive strength.

The graphite particles contained in the first layer 52 a may be particles of, for example, natural graphite or artificial graphite. For example, the content of graphite particles is preferably 85 mass % or greater, preferably 90 mass % or greater relative to the total amount of the first layer 52 a. The negative-electrode active material particles P1 constituting the first layer 52 a may contain negative-electrode active material particles other than graphite particles and the Si particles without lessening the effect of the present disclosure.

The negative-electrode active material particles P2 constituting the second layer 52 b may be any material particles capable of reversibly occluding and releasing lithium ions. For example, the particles may contain carbon materials such as natural graphite, artificial graphite, non-graphitizable carbon, and graphitizable carbon; surface-modified carbon materials that are carbon materials covered with amorphous carbon films; metals alloyed with lithium, e.g., silicon (Si) and tin (Sn), or alloys containing metallic elements such as Si and Sn; or compounds containing metallic elements such as Si and Sn. However, if the second layer 52 b near the surface contains a large amount of compounds other than carbon materials, such as Si compounds of the lithium silicate particles and the silicon carbon composite particles or Sn compounds, the reductive decomposition of an electrolytic solution is likely to occur during the high-temperature storage of the nonaqueous-electrolyte secondary battery. Thus, the second layer 52 b desirably contains few compounds other than carbon materials. For example, compounds other than carbon materials preferably account for at most 1 mass % relative to the total amount of the negative-electrode active material layer 52.

The first layer 52 a preferably contains 0.01 mass % to 0.4 mass % of a carbon nanotube having one to five graphene sheets and more preferably contains 0.02 mass % to 0.3 mass % of the carbon nanotube, in view of suppression of deterioration of charge and discharge cycle characteristics regarding the nonaqueous-electrolyte secondary battery, for example. In this case, a graphene sheet means a layer in which the carbon atoms of an sp2 hybridized orbital making up graphite crystals are located at the apexes of a regular hexagon. A carbon nanotube having a single graphene sheet is generally called a single-walled carbon nanotube (SWCNT) with a carbon nanostructure in which a single graphene sheet constitutes a single cylindrical shape. A carbon nanotube having at least two graphene sheets is generally called a multi-walled carbon nanotube with a carbon nanostructure in which multiple graphene sheets are concentrically stacked to constitute a single cylindrical shape. The first layer 52 a may include a carbon nanotube having at least six graphene sheets. The first layer 52 a preferably includes few carbon nanotubes, in consideration of suppression of a reduction in capacity in the charge and discharge cycle. The content of a carbon nanotube is preferably at most 0.01 mass % with respect to the first layer 52 a. The second layer 52 b may also contain a carbon nanotube (single-walled or multi-walled).

The second layer 52 b preferably has a larger porosity rate than the first layer 52 a. This may increase the penetration of an electrolytic solution into the negative-electrode active material layer 52 and contribute to, for example, suppression of an increase in resistance during high-rate charge and discharge, or suppression of a reduction in capacity in a charge and discharge cycle. The porosity rates of the first layer 52 a and the second layer 52 b are two-dimensional values, each being determined from the area ratio of pores between particles in each layer relative to the cross-sectional area of each layer. For example, the porosity rates are determined by the following steps.

-   -   (1) The negative electrode is partially cut, and then the         negative electrode is processed by an ion milling device (e.g.,         IM4000 by Hitachi High-Tech Corporation) so as to expose the         cross section of the negative-electrode active material layer         52.     -   (2) A reflection electron image of the cross section of the         first layer 52 a in the exposed negative-electrode active         material layer 52 is captured by using a scanning electron         microscope.     -   (3) The cross-sectional image obtained thus is captured by a         computer and is binarized using image analysis software (e.g.,         ImageJ by the National Institutes of Health), obtaining a binary         image in which the cross sections of particles in the         cross-sectional image are black and pores between particles and         pores in particles are white.     -   (4) The area of pores between particles in a measurement range         (50 μm×50 μm) is calculated from a binary image. The         cross-sectional area (2500 μm²=50 μm×50 μm) of the first layer         52 a is set as the measurement range, and the porosity rate of         the first layer 52 a (the area of pores between         particles×100/the cross-sectional area of the negative-electrode         active material layer 52) is calculated from the calculated area         of pores between particles.

The particle-internal porosity rate of the negative-electrode active material particles P2 and the porosity rate of the second layer 52 b are similarly measured.

A method of adjusting the porosity rates of the first layer 52 a and the second layer 52 b is, for example, a method of adjusting roll forces applied to the first coating and the second coating during the formation of the negative-electrode active material layer 52.

The compression modulus of the second layer 52 b is preferably at least 1.2 times and more preferably at least twice the compression modulus of the second layer 52 b. The satisfaction of the range may suppress, for example, an increase in resistance during high-rate charge and discharge.

The negative-electrode active material layer 52 has a thickness of, for example, 40 μm to 120 μm, preferably 50 μm to 90 μm on one side of the negative-electrode current collector 50. The thickness of the negative-electrode active material layer 52 is measured from a cross-sectional image of the negative electrode 38 b, the image being captured by a scanning electron microscope (SEM).

For the negative-electrode current collector 50, a metal leaf that is stable in the potential range of the negative electrode 38 b or a film having a metallic surface layer is used. For example, materials such as copper may be used.

The positive electrode 38 a includes, for example, a positive-electrode current collector and a positive-electrode active material layer formed on the positive-electrode current collector. For the positive-electrode current collector, a metal leaf that is stable in the potential range of the positive electrode or a film having a metallic surface layer is used. For example, aluminum or an aluminum alloy may be used. The positive-electrode active material preferably contains positive-electrode active material particles, a conductive material, and a binder and is preferably provided on both sides of the positive-electrode current collector. The positive electrode 38 a can be produced by, for example, applying a coating of positive-electrode mixture slurry containing a positive-electrode active material, a conductive material, and a binder to the positive-electrode current collector, drying the coating, and then compressing the coating into a positive-electrode active material layer on each side of the positive-electrode current collector.

The positive-electrode active material is, for example, a lithium-transition metal composite oxide. A lithium-transition metal composite oxide contains metallic elements such as Ni, Co, Mn, Al, B, Mg, Ti, V, Cr, Fe, Cu, Zn, Ga, Sr, Zr, Nb, In, Sn, Ta, and W. From among the metallic elements, at least one of Ni, Co, and Mn is preferably contained. A composite oxide is, for example, a lithium-transition metal composite oxide containing Ni, Co, and Mn or a lithium-transition metal composite oxide containing Ni, Co, and Al.

The separator 38 d is, for example, a porous sheet with ion permeation and insulation. Specific examples of a porous sheet include a microporous thin film, a woven fabric, and a nonwoven fabric. The separator 38 d is may be made of materials including olefin resins such as polyethylene and polypropylene and cellulose. The separator 38 d may be a stack including a cellulose fiber layer and a thermoplastic-resin fiber layer containing olefin resin. Alternatively, the separator 38 d may be a multilayer separator including a polyethylene layer and a polypropylene layer. The surface of the separator 38 d may be coated with materials such as aramid resin and ceramic.

The separator 38 d may have any compression modulus lower than that of the first layer 52 a of the negative-electrode active material layer 52. For example, the compression modulus is preferably 0.1 to 0.6 times, more preferably 0.15 to 0.5 times the compression modulus of the first layer 52 a in view of effective suppression of an increase in resistance during high-rate charge and discharge. The compression modulus of the separator 38 d is adjusted by controlling, for example, the selection of materials, a porosity rate, and a pore size.

The electrolytic solution is, for example, a nonaqueous electrolytic solution containing a supporting electrolyte in an organic solvent (nonaqueous solvent). The nonaqueous solvent may be a solvent containing, for example, esters, ethers, nitriles, or amides, or a mixed solvent containing at least two kinds of these compounds. The supporting electrolyte is, for example, a lithium salt such as LiPF₆.

The materials of the elastic body 40 include, for example, thermosetting elastomers such as natural rubber, polyurethane rubber, silicone rubber, and fluorocarbon rubber and thermoplastic elastomers such as polystyrene, olefin, urethane, polyester, and polyamide. These materials may be foamed materials. Moreover, a heat insulating material that supports porous materials such as silica xerogel may be used.

The elastic body 40 may have any compression modulus lower than that of the separator 38 d. For example, the compression modulus is preferably 120 MPa or less and is more preferably 80 MPa or less in view of effective suppression of an increase in resistance during high-rate charge and discharge.

The elastic body 40 may have a constant compression modulus in one plane but may vary in deformability in the plane as will be described below.

FIG. 7 is a schematic perspective view illustrating an example of the elastic body. The elastic body 40 in FIG. 7 has a soft portion 44 and hard portions 42. The hard portions 42 are placed on the outer edges of the elastic body 40 with respect to the soft portion 44. The elastic body 40 in FIG. 7 has a structure in which the hard portions 42 are disposed on both ends in the second direction Y and the soft portion 44 is disposed between the two hard portions 42. The soft portion 44 is preferably disposed so as to overlap the center of the long lateral faces of the housing 13 and the center of the electrode body 38 in the first direction X. The hard portions 42 are preferably disposed so as to overlap the outer edges of the long lateral faces of the housing 13 and the outer edge of the electrode body 38 in the first direction X.

As described above, the nonaqueous-electrolyte secondary battery 10 is expanded mainly by the expansion of the electrode body 38. The expansion of the electrode body 38 increases toward the center. Specifically, the displacement of the electrode body 38 increases toward the center in the first direction X and decreases from the center toward the outer edge. According to the displacement of the electrode body 38, the displacement of the nonaqueous-electrolyte secondary battery 10 increases toward the center of the long lateral face of the housing 13 in the first direction X and decreases from the center toward the outer edge of the long lateral face of the housing 13. Thus, if the elastic body 40 in FIG. 7 is placed in the housing 13, the elastic body 40 can receive, with the soft portion 44, a large load generated by a large displacement of the electrode body 38 and receive, with the hard portions 42, a small load generated by a small displacement of the electrode body 38. If the elastic body 40 in FIG. 7 is placed outside the housing 13, the elastic body 40 can receive, with the soft portion 44, a large load generated by a large displacement of the nonaqueous-electrolyte secondary battery 10 and receive, with the hard portions 42, a small load generated by a small displacement of the nonaqueous-electrolyte secondary battery 10.

The elastic body 40 in FIG. 7 has a recessed portion 46 in the first direction X. A non-recessed portion adjacent to the recessed portion 46 can be partially displaced to the recessed portion 46 when receiving a load from the nonaqueous-electrolyte secondary battery 10 or the electrode body 38. Thus, the provision of the recessed portion 46 can facilitate deformation of the non-recessed portion. In this configuration, in order to make the soft portion 44 more deformable than the hard portions 42, the area ratio of the recessed portion 46 to the area of the soft portion 44 is preferably larger than the area ratio of the recessed portion 46 to the area of the hard portions 42 in the first direction X. On the elastic body 40 in FIG. 7 , the recessed portion 46 is disposed only in the soft portion 44. The recessed portion 46 may be disposed in the hard portions 42.

The recessed portion 46 includes a core portion 46 a and a plurality of linear portions 46 b. The core portion 46 a is shaped like a circle disposed at the center of the elastic body 40 in the first direction X. The linear portions 46 b are radially extended from the core portion 46 a. Since the linear portions 46 b are radially extended, the ratio of the linear portions 46 b increases toward the core portion 46 a and the non-recessed portions decreases toward the core portion 46 a. Thus, the deformability of the non-recessed portions increases near the core portion 46 a.

The elastic body 40 may have a plurality of through holes penetrating the elastic body 40 in the first direction X, instead of or along with the recessed portion 46. The through holes are not illustrated. The provision of the through holes can facilitate deformation of non-penetrating portions. Hence, in order to make the soft portion 44 more deformable than the hard portions 42, the area ratio of the through holes to the area of the soft portion 44 is preferably larger than the area ratio of the through holes to the area of the hard portions 42 in the first direction X.

Another example of the elastic body will be described below.

FIG. 8 is a partial schematic cross-sectional view of the elastic body disposed between the electrode body and the housing. The elastic body 40 receives a load from the electrode body 38 in the stacking direction (first direction X) of the electrode body 38. The elastic body 40 includes a substrate 42 a where the hard portions 42 having predetermined hardness are formed, and the soft portion 44 that is softer than the hard portion 42. The hard portion 42 is a projecting portion that projects from the substrate 42 a toward the electrode body 38 and may be ruptured or plastically deformed by at least a predetermined load. The soft portion 44 is shaped like a sheet disposed between the substrate 42 a where the hard portions 42 are formed and the electrode body 38 near the electrode body 38. The soft portion 44 is separated from the electrode body 38. The soft portion 44 has through holes 44 a at positions overlapping the hard portions 42 in the first direction X. The hard portion 42 is inserted into the through hole 44 a, and the tip of the hard portion 42 projects from the soft portion 44.

In response to a change of the shapes of the hard portions 42, the elastic body 40 shifts from a first state in which a load from the electrode body 38 is received by the hard portions 42 to a second state in which the load is received by the soft portion 44. In other words, in the elastic body 40, a load applied in the stacking direction of the electrode body 38 by the expansion of the electrode body 38 is received by the hard portions 42 (first state). Thereafter, if for some reason the amount of expansion of the electrode body 38 increases so as to apply an excessive load to the hard portions 42, the hard portions 42 is ruptured or plastically deformed, the electrode body 38 comes into contact with the soft portion 44, and the load in the stacking direction of the electrode body 38 is received by the soft portion 44 (second state).

In the case of an elastic body having asperities, the compression modulus is calculated as follows: the compression modulus (MPa)=a load (N)/a projection area (mm²) in the planar direction of the elastic body×(the modification (mm) of the elastic body/the thickness (mm) of the elastic body to a projecting portion).

EXAMPLES

The present disclosure will be further described in accordance with examples. The present disclosure is not limited to the examples.

Example 1

[Production of a Positive Electrode]A lithium-transition metal composite oxide expressed by the general formula LiNi_(0.82)Co_(0.15)Al_(0.03)O₂ was used as a positive-electrode active material. The positive-electrode active material, acetylene black, and polyvinylidene fluoride were mixed with a solid mass ratio of 97:2:1, and a positive-electrode mixture slurry was prepared by using N-methyl-2-pyrrolidone (NMP) as a dispersion medium. Subsequently, a coating of the positive-electrode mixture slurry was applied to each side of a positive-electrode current collector composed of aluminum foil. The coating was dried, rolled, and then cut into a predetermined electrode size, so that a positive electrode was obtained with a positive-electrode active material layer formed on each side of the positive-electrode current collector.

[Preparation of a First Negative-Electrode Mixture Slurry]

Graphite particles having a BET specific surface area of 1.5 m²/g, lithium silicate particles (LiSiO), a single-walled carbon nanotube, the dispersion of styrene-butadiene rubber (SBR), and sodium carboxymethylcellulose (CMC-Na) were mixed at a solid mass ratio of 76:24:0.01:1:1, and the first negative-electrode mixture slurry was prepared by using water as a dispersion medium.

[Preparation of a Second Negative-Electrode Mixture Slurry]

Graphite particles having a BET specific surface area of 2.9 m²/g, the dispersion of SBR, and CMC-Na were mixed at a solid mass ratio of 100:1:1.5, and the second negative-electrode mixture slurry was prepared by using water as a dispersion medium.

[Production of a Negative Electrode]

A coating of the first negative-electrode mixture slurry was applied to each side of the negative-electrode current collector composed of copper foil, the coating was dried and rolled, a coating of the second negative-electrode mixture slurry was applied onto the coating, and the coating was dried and rolled, so that a negative-electrode active material layer was formed with a first layer of the first negative-electrode mixture slurry and a second layer of the second negative-electrode mixture slurry on the negative-electrode current collector. The negative-electrode active material layer was cut into a predetermined electrode size so as to obtain a negative electrode. The negative-electrode active material layer having a thickness of 160 μm (except for the negative-electrode current collector) was formed with an equal amount of application of the first and second negative-electrode mixture slurry. The content of the lithium silicate particles was 12 mass % relative to the total amount of the negative-electrode active material layer. During the production of the negative electrode, the measured compression moduli of the first and second layers were 750 MPa and 900 MPa.

[Preparation of an Electrolytic Solution]

Ethylene carbonate (EC), methyl ethyl carbonate (EMC), and dimethyl carbonate (DMC) were mixed at a volume ratio of 3:3:4. An electrolytic solution was prepared by dissolving LiPF₆ at a concentration of 1.4 mol/L in the mixed solvent.

[Production of the Nonaqueous-Electrolyte Secondary Battery]

Negative electrodes, separators with a compression modulus of 120 MPa, and positive electrodes were sequentially stacked to produce an electrode body. The negative electrodes and the positive electrodes were connected to the positive terminal and the negative terminal and were stored in an exterior part including an aluminum laminate. After the electrolytic solution was poured into the exterior part, the opening of the exterior part was sealed, so that the nonaqueous-electrolyte secondary battery was produced.

The produced nonaqueous-electrolyte secondary battery was held by a pair of elastic bodies (a urethane foam having a compression modulus of 60 MPa) and was held and fixed by a pair of end plates, so that the secondary battery module was produced.

Example 2

The secondary battery module was produced as in Example 1 except that graphite particles having a BET specific surface area of 1.5 m²/g, silicon carbon composite particles (Si_(0.4)C_(0.6)), a single-walled carbon nanotube, the dispersion of styrene-butadiene rubber (SBR), and sodium carboxymethylcellulose (CMC-Na) were mixed at a solid mass ratio of 76:24:0.01:1:1.5 in the preparation of the first negative-electrode mixture slurry. The content of the silicon carbon composite particles was 12 mass % relative to the total amount of the negative-electrode active material layer. During the production of the negative electrode, the measured compression moduli of the first and second layers were 700 MPa and 900 MPa.

Example 3

The secondary battery module was produced as in Example 1 except that graphite particles having a BET specific surface area of 1.5 m²/g, lithium silicate particles (LiSiO), a single-walled carbon nanotube, the dispersion of styrene-butadiene rubber (SBR), and sodium carboxymethylcellulose (CMC-Na) were mixed at a solid mass ratio of 76:24:0.4:1:1.5 in the preparation of the first negative-electrode mixture slurry. The content of the lithium silicate particles was 12 mass % relative to the total amount of the negative-electrode active material layer. During the production of the negative electrode, the measured compression moduli of the first and second layers were 750 MPa and 900 MPa.

Example 4

The secondary battery module was produced as in Example 1 except that mixed graphite particles prepared by mixing graphite particles having an average particle diameter of 8 μm and graphite particles having an average particle diameter of 18 μm at a mass ratio of 4:6, lithium silicate particles (LiSiO), a single-walled carbon nanotube, the dispersion of styrene-butadiene rubber (SBR), and sodium carboxymethylcellulose (CMC-Na) were mixed with a solid mass ratio of 76:24:0.01:1:1.5 in the preparation of the first negative-electrode mixture slurry. The measured BET specific surface area of the mixed graphite was 2.5 m²/g. The content of the lithium silicate particles was 12 mass % relative to the total amount of the negative-electrode active material layer. During the production of the negative electrode, the measured compression moduli of the first and second layers were 700 MPa and 900 MPa.

Example 5

The secondary battery module was produced as in Example 1 except that mixed graphite particles prepared by mixing graphite particles having a particle compressive strength of 60 MPa and graphite particles having a particle compressive strength of 15 MPa at a mass ratio of 6:4, lithium silicate particles (LiSiO), a single-walled carbon nanotube, the dispersion of styrene-butadiene rubber (SBR), and sodium carboxymethylcellulose (CMC-Na) were mixed at a solid mass ratio of 76:24:0.4:1:1.5 in the preparation of the first negative-electrode mixture slurry. The measured BET specific surface area of the mixed graphite was 2.5 m²/g. The content of the lithium silicate particles was 12 mass % relative to the total amount of the negative-electrode active material layer. During the production of the negative electrode, the measured compression moduli of the first and second layers were 650 MPa and 900 MPa.

Comparative Example 1

The nonaqueous-electrolyte secondary battery was produced as in Example 1 except that graphite particles having a BET specific surface area of 4.5 m²/g, lithium silicate particles (LiSiO), a multi-walled carbon nanotube having five graphene sheets, the dispersion of styrene-butadiene rubber (SBR), and sodium carboxymethylcellulose (CMC-Na) were mixed at a solid mass ratio of 76:24:1:1:1.5 in the preparation of the first negative-electrode mixture slurry. The content of the lithium silicate particles was 12 mass % relative to the total amount of the negative-electrode active material layer. During the production of the negative electrode, the measured compression moduli of the first and second layers were 550 MPa and 900 MPa.

The produced nonaqueous-electrolyte secondary battery was held and fixed by a pair of end plates, so that the secondary battery module was produced. In other words, the elastic body was not disposed between the nonaqueous-electrolyte secondary battery and the end plate.

Comparative Example 2

The nonaqueous-electrolyte secondary battery produced in Comparative Example 1 was held by a pair of elastic bodies (a urethane foam having a compression modulus of 60 MPa) and was held and fixed by a pair of end plates, so that the secondary battery module was produced.

[Measurement of an Initial Resistance (IV Resistance)]

The initial resistances of the secondary battery modules according to the examples and the comparative examples were measured under the following conditions: The secondary battery module adjusted in a charging state of SOC 60% was subjected to constant current discharge at a temperature of 25° C. at 2 C rate for ten seconds, so that a voltage drop (V) was calculated. The value (V) of the voltage drop was divided by a corresponding current value (I) to calculate an IV resistance (mΩ), and then the mean value of the resistance was determined as an initial resistance.

[High-Rate Charge and Discharge Test]

Subsequently, for the secondary battery modules according to the examples and the comparative examples, a charge and discharge cycle test was conducted such that ten cycles of charge and discharge were repeated at a temperature of 25° C. After the cycle test, a resistance increase rate was measured. In one cycle of the charge and discharge cycle test, constant current charge was performed at a charge rate of 1.5 C for 4300 seconds, the charge was suspended for ten seconds, constant current discharge was performed at a discharge rate of 1.5 C for 4300 seconds, and then the discharge was suspended for ten seconds. Subsequently, the resistances (IV resistances) of the secondary battery modules after the charge and discharge cycle test were measured by the same method as the measurement of the initial resistance, and a resistance increase rate was measured. The test was repeated until the rate of increase reached 200%. Thereafter, the effect of suppressing an increase in resistance during high-rate charge and discharge was evaluated based on the following evaluation criteria:

◯: The number of cycles necessary for obtaining a resistance increase rate exceeding 200% is at least 80 cycles

x: The number of cycles necessary for obtaining a resistance increase rate exceeding 200% is less than 80 cycles

[Initial Discharged-Capacity Measurement Test]

For the secondary battery modules of the examples and the comparative examples in an initial state, constant current charge was performed until a battery voltage reached 4.2 V at a constant current value of ⅓ A, constant current discharge was performed until the battery voltage reached 2.5 V at a constant current value of ⅓ A, and then an initial discharged capacity was measured.

[High-Temperature Storage Test]

For the secondary battery modules of the examples and the comparative examples after the initial discharged-capacity measurement test, constant current charge was performed until a battery voltage reached 4.2 V at a constant current value of ⅓ A, and then each battery was stored in a thermostat at 60° C. for sixty days. After sixty days, each battery was collected, and then a discharged capacity after the high-temperature storage was measured like an initial capacity. The discharged capacity after the high-temperature storage was divided by the initial discharged capacity, so that a capacity recovery rate was calculated.

Table 1 shows the test results of the examples and the comparative examples.

TABLE 11 NEGATIVE-ELECTRODE ACTIVE MATERIAL LAYER FIRST LAYER CARBON SECOND LAYER NANOTUBE GRAPHITE GRAPHITE THE PARTICLES COMPRESSION PARTICLE COMPRESSION NUMBER BET MODULUS BET MODULUS OF (m²/g) (MPa) (m²/g) (MPa) LAYERS CONTENT EXAMPLE 1 2.9 900 1.5 750 1 0.01 wt % EXAMPLE 2 2.9 900 1.5 750 1 0.01 wt % EXAMPLE 3 2.9 900 1.5 750 1  0.4 wt % EXAMPLE 4 2.9 900 2.5 700 1  0.4 wt % (AVERAGE PARTICLE DIAMETER 8 um, 18 um) EXAMPLE 5 2.9 900 2.5 650 1  0.4 wt % (COMPRESSIVE STRENGTH 60 MPa, 15 MPa) COMPARATIVE 2.9 900 4.5 550 5   1 wt % EXAMPLE 1 COMPARATIVE 2.9 900 4.5 550 5   1 wt % EXAMPLE 2 NEGATIVE- TEST RESULT ELECTRODE EFFECT OF ACTIVE SUPPRESSING MATERIAL INCREASE IN CAPACITY LAYER RESISTANCE RECOVERY FIRST LAYER SEPARATOR ELASTIC BODY DURING HIGH- RATE AFTER CONTENT COMPRESSION COMPRESSION RATE CHARGE HIGH- OF Si MODULUS MODULUS AND TEMPERATURE PARTICLES (MPa) (MPa) DISCHARGE STORAGE (%) EXAMPLE 1 LiSi0 120 60 ○ 91 12 wt % EXAMPLE 2 Si_(0.4)C_(0.6) 120 60 ○ 89 12 wt % EXAMPLE 3 LiSi0 120 60 ○ 89 12 wt % EXAMPLE 4 LiSi0 120 60 ○ 89 12 wt % EXAMPLE 5 LiSi0 120 60 ○ 89 12 wt % COMPARATIVE LiSi0 120 0 × 87 EXAMPLE 1 12 wt % COMPARATIVE LiSi0 120 60 ○ 80 EXAMPLE 2 12 wt %

According to Examples 1 to 5 in which a compression modulus satisfies the relationship of the second layer near the surface>the first layer near the negative-electrode current collector>the separator>the elastic body, graphite particles contained in the first layer have a BET specific surface area of 1 to 2.5 m²/g, and the first layer contains 12 mass % of Si particles (lithium silicate particles or SiC particles), so that an increase in resistance during high-rate charge and discharge and a reduction in capacity recovery rate after the high-temperature storage are suppressed as compared with Comparative Examples 1 and 2 that do not satisfy the foregoing requirements.

REFERENCE SIGNS LIST

-   1 Secondary battery module -   2 Stack -   4 End plate -   6 Locking member -   8 Cooling plate -   10 Nonaqueous-electrolyte secondary battery -   12 Insulating spacer -   13 Housing -   14 Outer can -   16 Sealing plate -   18 Output terminal -   38 Electrode body -   38 a Positive electrode -   38 b Negative electrode -   38 d Separator -   39 Winding core -   40 Elastic body -   42 Hard portion -   42 a Substrate -   44 soft portion -   44 a Through hole -   46 Recessed portion -   46 a Core portion -   46 b Linear portion -   50 Negative-electrode current collector -   52 Negative-electrode active material layer -   52 a First layer -   52 b Second layer 

The invention claimed is:
 1. A secondary battery module comprising: at least one nonaqueous-electrolyte secondary battery, and an elastic body that is placed with the nonaqueous-electrolyte secondary battery and receives a load from the nonaqueous-electrolyte secondary battery in a placement direction of the elastic body, wherein the nonaqueous-electrolyte secondary battery includes an electrode body in which a positive electrode, a negative electrode, and a separator disposed between the positive electrode and the negative electrode are stacked, and a housing accommodating the electrode body, the negative electrode includes a negative-electrode current collector, and a negative-electrode active material layer that is formed on the negative-electrode current collector and contains negative-electrode active material particles, the negative-electrode active material layer including a first layer formed on the negative-electrode current collector, and a second layer that is formed on the first layer and has a higher compression modulus than the first layer, the separator has a lower compression modulus than the first layer, the elastic body has a lower compression modulus than the separator, the negative-electrode active material particles contained in the first layer include graphite particles and at least one Si particle selected from the group consisting of lithium silicate particles and silicon carbon composite particles, the graphite particles contained in the first layer have a BET specific surface area of 1 to 2.5 m²/g, and a content of the Si particles is 6 mass % to 13 mass % relative to a total amount of the negative-electrode active material layer.
 2. The secondary battery module according to claim 1, wherein the first layer contains 0.01 mass % to 0.4 mass % of a carbon nanotube having one to five graphene sheets.
 3. The secondary battery module according to claim 1, wherein the graphite particles contained in the first layer include two kinds of graphite particles having different average particle diameters, graphite particles (A) have a larger average particle diameter than graphite particles (B), and a ratio of the average particle diameter of graphite particles (B) to the average particle diameter of graphite particles (A) is 0.3 to 0.5.
 4. The secondary battery module according to claim 1, wherein the graphite particles contained in the first layer include two kinds of graphite particles having different particle compressive strengths, graphite particles (C) have a larger particle compressive strength than graphite particles (D), a ratio of the particle compressive strength of graphite particles (D) to the particle compressive strength of graphite particles (C) is 0.2 to 0.6, and graphite particles (D) have a particle compressive strength of 10 MPa 35 MPa.
 5. The secondary battery module according to claim 1, wherein the second layer has a higher porosity rate than the first layer.
 6. The secondary battery module according to claim 1, wherein the elastic body has a compression modulus of at most 120 MPa.
 7. A nonaqueous-electrolyte secondary battery comprising: an electrode body in which a positive electrode, a negative electrode, and a separator disposed between the positive electrode and the negative electrode are stacked, an elastic body configured to receive a load from the electrode body in a stacking direction of the electrode body, and a housing accommodating the electrode body and the elastic body, wherein the negative electrode includes a negative-electrode current collector, and a negative-electrode active material layer that is formed on the negative-electrode current collector and contains negative-electrode active material particles, the negative-electrode active material layer including a first layer formed on the negative-electrode current collector and a second layer that is formed on the first layer and has a higher compression modulus than the first layer, the separator has a lower compression modulus than the first layer, the elastic body has a lower compression modulus than the separator, the negative-electrode active material particles contained in the first layer include graphite particles and at least one Si particle selected from the group consisting of lithium silicate particles and silicon carbon composite particles, the graphite particles contained in the first layer have a BET specific surface area of 1 to 2.5 m²/g, and a content of the Si particles is 6 mass % to 13 mass % relative to a total amount of the negative-electrode active material layer. 